Moisturecuring Zinc- Rich Anticorrosive primers

Moisturecuring Epoxy Zinc-Rich Anticorrosive primers
Characteristics: when the air humidity reached 94%, it can still firmed be film, cathodic protection、excellent rust resistance and anticorrosive property, quickly dry, perfect adhesion with steel surface which after abrasive blasting handle it, abrasion resistance, good attack resistance, short coating interval, excellent torch cutting and weldability property.
Uses: Mainly use for anticorrosive steel structure in South high humidity area, also use for the anticorrosion of offshore platform、new-built boats etc. in high humidity environment.
Technical target：
Mixing ratio:                           Host crystal/ Firming agent=10/1 (by weight)
Standard film thickness:       dry: 50μm/coat
Academic spreading rate:   0.18kg/ m2/50μm
Solid contents:                      80%
Humidity requirement:        below 94%
Drying time & Coating interval

Substrate treatment：Remove rust、oxide skin and shop primer by abrasive blasting, reached ISO Sa2.5 grade.
Matching：
Applicable substrate: Unpainted steel
Applicable upper coatings: Match with kinds of epoxy、polyurethane、rubber、asphalt paints.

 

More Detail:

Material To make sure the quality, we imported parts of the raw material, titanium black from Germany, curing agent from the United States, titanium dioxide from Japan and the USA, and  the  acrylic resin from the UAS . We are committed to providing the best product.

Workshop Our factory bulit strictly with ISO standrads, which boasts the best facilities in China.With advanced production technology, technical equipment, integrated and scientific quality control system. Our products are loved by different customers and have benn sold wordwide

Inspection Each batch of the paints should go through very strict ly inspection before they leave the factory, Our company product guarantees the quality, achieves the related nation profession standard and the enterprise standard.