Moisturecuring  Epoxy Mica Iron Intermediate Coat

Characteristics: When air humidity reached 94%, it can still firmed be film normally, physical and chemical property unchangeable, dry quickly, excellent compatibility with kinds of zinc and epoxy powder, good shielding property.
Uses: Mainly use for anticorrosion of steel structure in hige humidity area and anticorrosion of offshore platform、cabin、ballast tank etc. in hige humidity area.
Technical target：
Mixing rate:                               Host crystal/Firming agent=8/1 (by weight)
Standard film thickness:        Dry: 50μm/coat
Academic spreading rate:      0.13kg/ m2/50μm
Solid contents:                        77%
Humidity requirement:           below 94%
Drying time & Coating interval

Substrate treatment：Remove zinc salt and other contaminant on primer surface.
Matching：
Applicable substrate: Zinc powder primer、Epoxy primer
Applicable upper coatings: Compatible with kinds of finishes

 

More Detail:

Material To make sure the quality, we imported parts of the raw material, titanium black from Germany, curing agent from the United States, titanium dioxide from Japan and the USA, and  the  acrylic resin from the UAS . We are committed to providing the best product.

Workshop Our factory bulit strictly with ISO standrads, which boasts the best facilities in China.With advanced production technology, technical equipment, integrated and scientific quality control system. Our products are loved by different customers and have benn sold wordwide

Inspection Each batch of the paints should go through very strict ly inspection before they leave the factory, Our company product guarantees the quality, achieves the related nation profession standard and the enterprise standard.